Zirconia ke thepa e nang le matla a phahameng a mochine le ho robeha ho thata ka mocheso oa kamore. Zirconia ea rona (ZrO2) e kenyelelitsoe ka 3mol% Y2O3 zirconia e tsitsitseng e tsitsitseng (PSZ). Hobane bophara ba karoloana ea thepa ea PSZ e nyane, e ka sebetsoa ka nepo e phahameng, mme ts'ebeliso ea eona likarolong tse nepahetseng tsa machining joalo ka hlobo e ntse e hola. Ntle le moo, e ka sebelisoa bakeng sa lisebelisoa tsa indasteri, likarolo tsa sehokelo sa optical le lisebelisoa tse silakanyang. The high fracture toughness of PSZ e ka sebelisoa ho etsa liliba tse khethehileng, hape e sebelisoa haholo ka lithipa tsa ceramic tsa malapeng, slicer le likarolo tse ling.
Thepa Thepa
| Ntho | 95% Alumina | 99% Alumina | Zirconia | Silicon carbide | SiliconeNitride | AluminiumNitride | Ceramic e sebetsang |
| Mmala | tšoeu | Bosehla bo kganyang | tšoeu | ntsho | ntsho | bohlooho | tšoeu |
| Boima ba 'mele (g/cm3) | 3.7g/cm3 | 3.9g/cm3 | 6.02g/cm3 | 3.2g/cm3 | 3.25g/cm3 | 3.2g/cm3 | 2.48g/cm3 |
| Ho Monyeha ha Metsi | 0% | 0% | 0% | 0% | 0% | 0% | 0% |
| Ho thatafala(HV) | 23.7 | 23.7 | 16.5 | 33 | 20 | - | - |
| Flexural Strength(MPa) | 300MPa | 400MPa | 1100MPa | 450MPa | 800MPa | 310MPa | 91MPa |
| Compressive Strength(MPa) | 2500MPa | 2800MPa | 3600MPa | 2000MPa | 2600MPa | - | 340MPa |
| Modulus ea Mocha ea Elasticity | 300GPa | 300GPa | 320GPa | 450GPa | 290GPa | 310 ~ 350GPa | 65GPa |
| Karolelano ea Poisson | 0.23 | 0.23 | 0.25 | 0.14 | 0.24 | 0.24 | 0.29 |
| Thermal Conductivity | 20W/m°C | 32W/m°C | 3W/m°C | 50W/m°C | 25W/m°C | 150W/m°C | 1.46W/m°C |
| Matla a Dielectric | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm |
| Ho hanyetsa Bophahamo(25℃) | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm | >105Ω·cm | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm |
Zirconia (ZrO2) Ke sebelisa haholo
Lisebelisoa tsa hlobo le hlobo (liforomo tse fapa-fapaneng, mokhoa o nepahetseng oa ho beha maemo, ho kenya letsoho); Likarolo tsa Mill (classifier, leloala la phallo ea moea, leloala la lifaha); Sesebelisoa sa indasteri (seha sa indasteri, mochini oa slitter, moqolo oa khatiso o bataletseng); Likarolo tsa sehokelo sa Optical (ring ea ho tiisa, sleeve, sebopeho sa V-groove); Selemo se khethehileng (coil spring, plate spring); Lihlahisoa tsa bareki (screwdriver tse nyane tse insulated, thipa ea ceramic, slicer).